www.melanexjou.fora.pl

[px231858]

Clean-cut, such as a new type of ceramic tile inlay


Paper introduces the system of tile method, based on sintering does not occur between the glaze and glaze fusion, pattern cut, as if embedded in the base into the glaze. Law point below. Choice of two glazes, one was transparent after firing, one for the glaze. To which the high melting temperature, and in both the molten state (back temperature) 'under the viscosity of the glaze with the glaze for the pattern, and the other based glaze. The basis of first imposing brick surface enamel, the formation of a certain thickness of the glaze layer, and then in the basic pattern of the glaze with a glaze layer on the drawing pattern, after the pattern of enamel softening melting temperature sintering, using patterns based enamel glaze and the melting temperature between When the viscosity difference and inclusion poor, so that the graphic pattern glazed draw cut, such as being embedded in the base enamel. Patterns can also be coated with the glaze on the brick cut the throat, and then cast a base glaze, but this time must be based on a transparent glaze, enamel, sintered base effect and be painted the same glaze. The pattern of softening the glaze melting temperature higher than the base glaze, usually a high viscosity melt temperature is also large, in the sintering process, when the base melt the glaze begins to soften, the softening of the above has not yet began to melt the glaze settlement patterns cut the throat into the basis of the glaze , and because the thickness of the glaze was charged with shop based in a scale, when the pattern of softening melting of the glaze, the enamel surface with the underlying pattern can be in the same smooth surface enamel surface. And because both melting (with temperature change), the pattern based enamel glaze viscosity ratio larger contact interface between the phenomenon of merging does not occur. If the pattern of enamel glaze applied on the basis of party, do not place the settlement process, the rest of the conditions and effects are the same. Embodiment to 6O% (weight) glass materials and 4og (weight) of feldspar made of transparent glaze, Serge test taper is SK5 ~ SK6ao to 10o copies (by weight) glass materials, and 65 (weight) set into the glaze color system , Serge test taper is SK4 ~ SK5-, which glaze melting point lower than the glaze, the melt viscosity smaller than the transparent glaze. Therefore, in this case as a pattern with a transparent glaze glaze, the glaze with a glaze based. Thermal expansion coefficient based glaze should weld the thermal expansion coefficient of the object similar to adobe. First with the hood painted enamel coating method based on the brick. Brick square with a side length of 150 blood iIl, thickness 7mm. Each glazed brick to make the basis of rejection capacity 26g, enamel thickness of 0.6mm. Then, with the screen printing method in the base glaze layer above impose O. . 5mm thick enamel pattern. Patterns have begun to soften the glaze to melt temperature (1180 In the heating process, the basis of the first melt the glaze, the pattern on the front of the glaze has not yet fused to the base: glazed settlement when the temperature reaches 1180 ℃, the pattern of the glaze melt,[link widoczny dla zalogowanych], two flush on the surface before the glaze, and integration between the contact interface does not occur phenomenon, described the graphic pattern glazed to maintain a distinct profile, and generally glass quality, softening temperature, high thermal expansion coefficient, therefore, softening of the melting of the grain depicted in graphic, but also keeps the original look. Fu Ying Quoted and Japan, New post attachments}! Glass Ying glass ornaments: This paper presents a show like tie-dye or color pattern of the new glass halo, can be widely used for furniture, buildings, plaques and other decorative box. Its system of law points are: the same expansion coefficient with numerous small pieces of glass and glass powder burn with fins placed on the furnace refractories, heat to completely melt the glass powder, glass block only the surface layer melted, to be slowly cooled materials outline visions clear if the new tiles embedded 0SgggSSggSSgg $ Sg